High photosensitivity 2D-few-layered molybdenum diselenide phototransistors

Date:
December 8, 2014
Source:
Toyohashi University of Technology
Summary:
Researchers have fabricated High photosensitivity back-gated field-effect phototransistors made of only 20 nanometer thick molybdenum diselenide crystals by facile mechanical cleavage and transfer of MoSe2 flakes onto a silicon wafers for next generation for photodetector applications.
Share:
FULL STORY

Two-dimensional (2D) layered materials are now attracting a lot of interest due to their unique optoelectronic properties at atomic thicknesses. Among them, graphene has been mostly investigated, but the zero-gap nature of graphene limits its practical applications. Therefore, 2D layered materials with intrinsic band gaps such as MoS2, MoSe2, and MoTe2 are of interest as promising candidates for ultrathin and high-performance optoelectronic devices.

Here, Pil Ju Ko and colleagues at Toyohashi University of Technology, Japan have fabricated back-gated field-effect phototransistors made of MoSe2 crystals having a thickness of only twenty nanometers. The devices were fabricated by mechanical cleavage of MoSe2 crystals into few-layered flakes, followed by transfer onto a silicon wafer with pre-deposited titanium electrodes.

Despite their ultra-thin physical size, the devices showed excellent field-effect phototransistor characteristics. The measured photoresponsivity of 97.1 AW-1 at zero back gate voltage was higher than previous reports of photodetectors fabricated using GaS, GaSe, MoS2, and InSe. The photoresponse of the MoSe2 was much faster (less than 15 msec) than ultrasensitive photodetectors based on monolayer MoS2. Furthermore, the theoretical external quantum efficiency was 280-fold higher than of commercial Si and InGaAs photodiodes.

The research shows that MoSe2 is a promising material for photodetector applications. The group is optimization the device performance by studying thickness-dependent of the photosensitivity.


Story Source:

Materials provided by Toyohashi University of Technology. Note: Content may be edited for style and length.


Journal Reference:

  1. A Abderrahmane, P J Ko, T V Thu, S Ishizawa, T Takamura, A Sandhu. High photosensitivity few-layered MoSe2 back-gated field-effect phototransistors. Nanotechnology, 2014; 25 (36): 365202 DOI: 10.1088/0957-4484/25/36/365202

Cite This Page:

Toyohashi University of Technology. "High photosensitivity 2D-few-layered molybdenum diselenide phototransistors." ScienceDaily. ScienceDaily, 8 December 2014. <www.sciencedaily.com/releases/2014/12/141208105427.htm>.
Toyohashi University of Technology. (2014, December 8). High photosensitivity 2D-few-layered molybdenum diselenide phototransistors. ScienceDaily. Retrieved March 18, 2024 from www.sciencedaily.com/releases/2014/12/141208105427.htm
Toyohashi University of Technology. "High photosensitivity 2D-few-layered molybdenum diselenide phototransistors." ScienceDaily. www.sciencedaily.com/releases/2014/12/141208105427.htm (accessed March 18, 2024).

Explore More

from ScienceDaily

RELATED STORIES