Substrate patterning creates p-n junctions in graphene

December 10, 2012
Georgia Institute of Technology, Research Communications
Researchers are creating graphene p-n junctions by transferring films of the electronic material to substrates that have been patterned by compounds that are either strong electron donors or electron acceptors.

Georgia Tech postdoctoral fellow Hossein Sojoudi holds a wafer containing graphene p-n junctions, while the screen display in the background shows electrical data measured in the devices.
Credit: Georgia Tech Photo: Gary Meek

The electronic properties of graphene films are directly affected by the characteristics of the substrates on which they are grown or to which they are transferred. Researchers are taking advantage of this to create graphene p-n junctions by transferring films of the promising electronic material to substrates that have been patterned by compounds that are either strong electron donors or electron acceptors.

Related Articles

A low temperature, controllable and stable method has been developed to dope graphene films using self-assembled monolayers (SAM) that modify the interface of graphene and its support substrate. Using this concept, a team of researchers at the Georgia Institute of Technology has created graphene p-n junctions -- which are essential to fabricating devices -- without damaging the material's lattice structure or significantly reducing electron/hole mobility.

The graphene was grown on a copper film using chemical vapor deposition (CVD), a process that allows synthesis of large-scale films and their transfer to desired substrates for device applications. The graphene films were transferred to silicon dioxide substrates that were functionalized with the self-assembled monolayers.

Information about creating graphene p-n junctions using self-assembled monolayers was presented on November 28, 2012 at the Fall Meeting of the Materials Research Society. Papers describing aspects of the work were also published in September 2012 in the journals ACS Applied Materials & Interfaces and the Journal of Physical Chemistry C. Funding for the research came from the National Science Foundation, through the Georgia Tech Materials Research Science and Engineering Center (MRSEC) and through separate research grants.

"We have been successful at showing that you can make fairly well doped p-type and n-type graphene controllably by patterning the underlying monolayer instead of modifying the graphene directly," said Clifford Henderson, a professor in the Georgia Tech School of Chemical & Biomolecular Engineering. "Putting graphene on top of self-assembled monolayers uses the effect of electron donation or electron withdrawal from underneath the graphene to modify the material's electronic properties."

The Georgia Tech research team working on the project includes faculty members, postdoctoral fellows and graduate students from three different schools. In addition to Henderson, professors who are part of the team include Laren Tolbert from the School of Chemistry and Biochemistry and Samuel Graham from the Woodruff School of Mechanical Engineering. The project team also includes Hossein Sojoudi, a postdoctoral fellow, and Jose Baltazar, a graduate research assistant.

Creating n-type and p-type doping in graphene -- which has no natural bandgap -- has led to development of several approaches. Scientists have substituted nitrogen atoms for some of the carbon atoms in the graphene lattice, compounds have been applied to the surface of the graphene, and the edges of graphene nanoribbons have been modified. However, most of these techniques have disadvantages, including disruption of the lattice -- which reduces electron mobility -- and long-term stability issues.

"Any time you put graphene into contact with a substrate of any kind, the material has an inherent tendency to change its electrical properties," Henderson said. "We wondered if we could do that in a controlled way and use it to our advantage to make the material predominately n-type or p-type. This could create a doping effect without introducing defects that would disrupt the material's attractive electron mobility."

Using conventional lithography techniques, the researchers created patterns from different silane materials on a dielectric substrate, usually silicon oxide. The materials were chosen because they are either strong electron donors or electron acceptors. When a thin film of graphene is placed over the patterns, the underlying materials create charged sections in the graphene that correspond to the patterning.

"We were able to dope the graphene into both n-type and p-type materials through an electron donation or withdrawal effect from the monolayer," Henderson explained. "That doesn't lead to the substitutional defects that are seen with many of the other doping processes. The graphene structure itself is still pristine as it comes to us in the transfer process."

The monolayers are bonded to the dielectric substrate and are thermally stable up to 200 degrees Celsius with the graphene film over them, Sojoudi noted. The Georgia Tech team has used 3-Aminopropyltriethoxysilane (APTES) and perfluorooctyltriethoxysilane (PFES) for patterning. In principle, however, there are many other commercially-available materials that could also create the patterns.

"You can build as many n-type and p-type regions as you want," Sojoudi said. "You can even step the doping controllably up and down. This technique gives you control over the doping level and what the dominant carrier is in each region."

The researchers used their technique to fabricate graphene p-n junctions, which was verified by the creation of field-effect transistors (FET). Characteristic I-V curves indicated the presence of two separate Dirac points, which indicated an energy separation of neutrality points between the p and n regions in the graphene, Sojoudi said.

The group uses chemical vapor deposition to create thin films of graphene on copper foil. A thick film of PMMA was spin-coated atop the graphene, and the underlying copper was then removed. The polymer serves as a carrier for the graphene until it can be placed onto the monolayer-coated substrate, after which it is removed.

Beyond developing the doping techniques, the team is also exploring new precursor materials that could allow CVD production of graphene at temperatures low enough to permit fabrication directly on other devices. That could eliminate the need for transferring the graphene from one substrate to another.

A low-cost, low-temperature means of producing graphene could also allow the films to find broader applications in displays, solar cells and organic light-emitting diodes, where large sheets of graphene would be needed.

"The real goal is to find ways to make graphene at lower temperatures and in ways that allow us to integrate it with other devices, either silicon CMOS or other materials that couldn't tolerate the high temperatures required for the initial growth," Henderson said. "We are looking at ways to make graphene into a useful electronic or opto-electronic material at low temperatures and in patterned forms."

This material is based on work supported by the National Science Foundation (NSF) under Grants CHE-0822697, CHE-0848833 and CMMI-0927736 and the Georgia Tech Materials Research Science and Engineering Center (MRSEC).

Story Source:

The above story is based on materials provided by Georgia Institute of Technology, Research Communications. The original article was written by John Toon. Note: Materials may be edited for content and length.

Journal References:

  1. Jose Baltazar, Hossein Sojoudi, Sergio A. Paniagua, Janusz Kowalik, Seth R. Marder, Laren M. Tolbert, Samuel Graham, Clifford L. Henderson. Facile Formation of Graphene P–N Junctions Using Self-Assembled Monolayers. The Journal of Physical Chemistry C, 2012; 116 (36): 19095 DOI: 10.1021/jp3045737
  2. Hossein Sojoudi, Jose Baltazar, Laren M. Tolbert, Clifford L. Henderson, Samuel Graham. Creating Graphene p–n Junctions Using Self-Assembled Monolayers. ACS Applied Materials & Interfaces, 2012; 4 (9): 4781 DOI: 10.1021/am301138v

Cite This Page:

Georgia Institute of Technology, Research Communications. "Substrate patterning creates p-n junctions in graphene." ScienceDaily. ScienceDaily, 10 December 2012. <www.sciencedaily.com/releases/2012/12/121210101414.htm>.
Georgia Institute of Technology, Research Communications. (2012, December 10). Substrate patterning creates p-n junctions in graphene. ScienceDaily. Retrieved March 1, 2015 from www.sciencedaily.com/releases/2012/12/121210101414.htm
Georgia Institute of Technology, Research Communications. "Substrate patterning creates p-n junctions in graphene." ScienceDaily. www.sciencedaily.com/releases/2012/12/121210101414.htm (accessed March 1, 2015).

Share This

More From ScienceDaily

More Matter & Energy News

Sunday, March 1, 2015

Featured Research

from universities, journals, and other organizations

Featured Videos

from AP, Reuters, AFP, and other news services

Rehab Robot Helps Restore Damaged Muscles and Nerves

Rehab Robot Helps Restore Damaged Muscles and Nerves

Reuters - Innovations Video Online (Mar. 1, 2015) A rehabilitation robot prototype to help restore deteriorated nerves and muscles using electromyography and computer games. Ben Gruber reports. Video provided by Reuters
Powered by NewsLook.com
Elon Musk's Hyperloop Moves Forward

Elon Musk's Hyperloop Moves Forward

Buzz60 (Feb. 27, 2015) Zipping around at 800-miles an hour is coming closer to reality in California. An entire town is being built around Elon Musk&apos;s Hyperloop concept and it wants you to stop in for a ride when it&apos;s ready. Brett Larson is on board. Video provided by Buzz60
Powered by NewsLook.com
Vibrating Bicycle Senses Traffic

Vibrating Bicycle Senses Traffic

Reuters - Innovations Video Online (Feb. 26, 2015) Dutch scientists have developed a smart bicycle that uses sensors, wireless technology and video to warn riders of traffic dangers. Ben Gruber reports. Video provided by Reuters
Powered by NewsLook.com
In Japan, Robot Dogs Are for Life -- And Death

In Japan, Robot Dogs Are for Life -- And Death

AFP (Feb. 25, 2015) Robot dogs are the perfect pet for some in Japan who go to repairmen-turned-vets when their pooch breaks down - while a full Buddhist funeral ceremony awaits those who don&apos;t make it. Duration: 02:40 Video provided by AFP
Powered by NewsLook.com

Search ScienceDaily

Number of stories in archives: 140,361

Find with keyword(s):
Enter a keyword or phrase to search ScienceDaily for related topics and research stories.


Breaking News:

Strange & Offbeat Stories

Space & Time

Matter & Energy

Computers & Math

In Other News

... from NewsDaily.com

Science News

Health News

Environment News

Technology News


Free Subscriptions

Get the latest science news with ScienceDaily's free email newsletters, updated daily and weekly. Or view hourly updated newsfeeds in your RSS reader:

Get Social & Mobile

Keep up to date with the latest news from ScienceDaily via social networks and mobile apps:

Have Feedback?

Tell us what you think of ScienceDaily -- we welcome both positive and negative comments. Have any problems using the site? Questions?
Mobile: iPhone Android Web
Follow: Facebook Twitter Google+
Subscribe: RSS Feeds Email Newsletters
Latest Headlines Health & Medicine Mind & Brain Space & Time Matter & Energy Computers & Math Plants & Animals Earth & Climate Fossils & Ruins